Effect of thermal treatment on zeolite for real-time gas sensing of oxygenated volatile organic compounds

Abstract

The breathable air is severally polluted due to the emission of various pollutants like volatile organic compounds (VOCs) and dust particles of submicron sizes. These pollutants have several adverse health hazards, which can cause fatal accidents and mortalities. In the current study, we have modified the FAU type of Zeolite (ZE) with the Si/Al to 1 and treated at different temperatures (300-600 degrees C) in a 10 percent H sub(2) + 90 percent N sub(2) mixture to achieve different distributions of oxygen vacancies. The presence of oxygen vacancy and electrons in the lattice is confirmed by EDAX, XPS and ESR techniques. The charge irregularities generated due to trapped electrons are exploited for detection of different VOCs like acetone, ethyl methyl ketone, isopropyl alcohol, ethanol, n-hexane, and benzene using the scanning kelvin probe (SKP) technique. The oxygen vacancies raise the distribution of Lewis and Brønsted basic sites, which impacts the interaction of VOCs with the sample surface and the amount of VOCs uptake. The untreated ZE and treated at 600 degrees C (ZE600) exhibited n-type behavior with 13.8 percent oxygen deficient sites with approx. 1.9 Mu mol/g of total basic sites and 3 Mu mol/g of total acidic sites. The thermal treatment for ZE600 leads to approx. 280 folds enhancement in surface photovoltage towards acetone with approx. 67 percent of recovery concerning untreated ZE.