Abstract:
Fe doped Ni sub(2)Mn sub(1.5)In sub(0.5), particularly, Ni sub(2)Mn sub(1.4)Fe sub(0.1)In sub(0.5), despite having an incommensurate, modulated 7M martensitic structure at room temperature exhibits frequency dependent behavior of storage modulus and loss which obeys the Vogel-Fulcher law as well as shows ergodicity breaking between zero field cooled and field cooled strain measurements just above the transition temperature. Both frequency dependence and ergodicity breaking are characteristics of a strain glassy phase and occur due to the presence of strain domains which are large enough to present signatures of long range martensitic order in diffraction but are non-interacting with other strain domains due to the presence of Fe impurities.